Color difference control measures. Factors causing color difference. First, because there is not enough preparation in the preparation process of construction materials, the color difference is caused by different batches of materials; Second, the construction personnel do not have a unified technical level, so in the spraying process, the thickness will be inconsistent, and some parts will be thinner, resulting in color difference; Third, excessive sand dropping in the spraying process, resulting in uneven particles, is also an important factor leading to color difference; Fourth, if the wall starts spraying after being exposed to the rain and does not wait until it is completely dry, it is very easy to cause color difference; Fifth, mainly because there is no uniform color difference in the process of color matching; Sixth, in the process of coating storage, it is easy to have delamination or floating color on the surface, but the color difference caused by spraying without stirring evenly before spraying.

控制色差出現(xiàn)的措施。，針對(duì)相同顏色、墻面，應(yīng)該保證真石漆的廠家、批號(hào)相同，并且要一次性采購(gòu)重組。如果相同顏色但批號(hào)不同，就應(yīng)該混勻后再進(jìn)行作業(yè)。采用從上下的噴涂方式，并且以墻面分隔縫、陰陽(yáng)角、水落管等作為分界線，進(jìn)行分段式的噴涂作業(yè)。第二，應(yīng)該積極通過(guò)培訓(xùn)等方式，提升施工人員的操作水平，從而保證施工中的噴涂更為均勻，形成一致的膜厚。第三，在噴涂過(guò)程中一般會(huì)因?yàn)閮煞矫嬖驅(qū)е碌羯斑^(guò)多，主要是因?yàn)樵谑┕ぶ袊姌尩臍鈮哼^(guò)大而導(dǎo)致，或者是噴槍移動(dòng)太快。

Measures to control color difference. First, for the same color and wall, we should ensure that the manufacturer and batch number of real stone paint are the same, and we should purchase and reorganize at one time. If the color is the same but the batch number is different, it should be mixed before operation. The spraying method from top to bottom is adopted, and the partition joints of the wall, internal and external corners, downspouts, etc. are used as the dividing line for segmented spraying operation. Second, we should actively improve the professional level of construction personnel through training, so as to ensure more uniform spraying in construction and form a consistent film thickness. Third, in the spraying process, too much sand will be dropped due to two reasons, mainly because the air pressure of the spray gun is too high during construction, or the spray gun moves too fast.

另外，就是涂料中兌水過(guò)多，從而涂料過(guò)稀而導(dǎo)致沙子上墻沒(méi)有足夠的初黏度。因此，應(yīng)該調(diào)整到合理的氣壓值，在噴涂的過(guò)程中掌握好噴槍移動(dòng)速度，盡可能不要兌水稀釋涂料。第四，在施工期間遇到雨水天氣，需要完全等到墻面干燥后再施工。第五，要調(diào)色達(dá)到足夠均勻。第六，在噴涂前，需要進(jìn)行均勻的攪拌。

In addition, there is too much water in the coating, so the coating is too thin, resulting in insufficient initial viscosity on the sand wall. Therefore, the air pressure should be adjusted to a reasonable value, the moving speed of the spray gun should be well controlled in the spraying process, and the paint should not be diluted with water as much as possible. Fourth, in case of rainy weather during construction, it is necessary to completely wait until the wall is dry before construction. Fifth, color matching should be uniform enough. Sixth, uniform stirring is required before spraying.

裂縫的控制措施。，針對(duì)陰陽(yáng)角裂縫的問(wèn)題來(lái)說(shuō)，因?yàn)殛庩?yáng)角是兩個(gè)面的交接，在真石漆干燥過(guò)程中會(huì)形成不同方向張力對(duì)陰陽(yáng)角處的涂膜產(chǎn)生作用力，進(jìn)而產(chǎn)生裂縫。如此需要用噴槍再覆蓋住裂縫，新噴涂的陰陽(yáng)角應(yīng)該注意不能一次噴涂太厚，應(yīng)該采用薄噴多層的方法，也就是等表面干燥后再?lài)娨淮危嚯x要足夠遠(yuǎn)，移動(dòng)的速度要快，不能垂直噴，只能采用散射的方式，讓霧化的邊緣掃入陰陽(yáng)角；

Crack control measures. Firstly, for the problem of cracks in internal and external corners, because the internal and external corners are the intersection of two surfaces, tension in different directions will be formed during the drying process of real stone paint, which will exert force on the film at the internal and external corners, and then produce cracks. In this way, it is necessary to cover the cracks with a spray gun. The internal and external corners newly sprayed should not be too thick at one time. The method of thin spraying and multi-layer spraying should be adopted, that is, spray again after the surface is dry. The distance should be far enough and the moving speed should be fast. Vertical spraying is not allowed. Only scattering can be used to sweep the atomized edge into the internal and external corners;

其次，如果在平面出現(xiàn)裂縫，一般來(lái)說(shuō)都是因?yàn)闇夭畲蠖鴮?dǎo)致，在內(nèi)外層干燥速度產(chǎn)生差異，進(jìn)而產(chǎn)生裂縫。這種情況應(yīng)該用小嘴噴槍采用薄噴多層方式，控制每層干燥速度，也要保證較遠(yuǎn)的噴涂距離；，如果在成膜的過(guò)程中產(chǎn)生裂縫，主要是因?yàn)閲娡扛采w不均勻?qū)е?，在涂層表面成膜后出現(xiàn)裂縫，也有可能是多個(gè)星期后才有裂縫出現(xiàn)，如此就要根據(jù)具體情況進(jìn)行具體分析，在施工過(guò)程中，要采用合理的盆土方法同時(shí)，要對(duì)配方進(jìn)行改變和試制。

Secondly, if cracks appear in the plane, generally speaking, they are caused by the large temperature difference, resulting in the difference in the drying speed of the inner and outer layers, resulting in cracks. In this case, the small nozzle spray gun should be used, and the thin spray multi-layer method should be adopted to control the drying speed of each layer and ensure a long spraying distance; Finally, if there are cracks in the process of film formation, it is mainly caused by uneven spraying coverage, and cracks appear on the coating surface after film formation, or cracks may not appear until several weeks later. In this way, specific analysis should be carried out according to the specific situation. In the construction process, reasonable basin soil method should be adopted, and the formula should be changed and trial produced.